Fluorine rubber composition and bladder for tire production

ABSTRACT

A fluorine rubber composition that provides high tensile strength and high elongation after vulcanization mutually compatible and from which favorable mechanical characteristics are obtained even in a high-temperature environment; and a bladder for tire production, which is manufactured using the same are provided. The fluorine rubber composition includes a rubber component containing a fluorine rubber and carbon black, wherein the carbon black has a specific surface area by nitrogen adsorption (N2SA) of 25 m2/g or more and not more than 180 m2/g and a dibutyl phthalate (DBP) absorption amount of 60 mL/100 g or more and not more than 180 mill 00 g; and in a kneading step (A) of compounding the carbon black in the rubber component, an average shear rate of a rotor surface of a kneading machine is 100 (1/sec) or more, and a kneading maximum temperature Tm is 120° C. or higher and not higher than 200° C.

TECHNICAL FIELD

The present invention relates to a fluorine rubber composition having excellent mechanical characteristics after vulcanization; and a bladder for tire production, which is manufactured using the same.

BACKGROUND ART

In recent years, fluorine rubbers are industrially used in broad fields centering on the automobile and machinery industries because they give rubber compositions which are excellent in terms of heat resistance, chemical resistance, and the like.

However, it may not be said that their mechanical characteristics are sufficient, and their application to fields where a high mechanical strength is required was limited.

On the contrary, Patent Document 1 proposes a combination of a fluorine rubber with an epichlorohydrin rubber; and Patent Document 2 discloses a fluorine rubber vulcanizable composition containing (A) a fluorine-containing elastomer copolymer composed of a vinylidene fluoride unit and at least one fluorine-containing monomer and containing iodine or bromine, the fluorine-containing elastomer copolymer having an intrinsic viscosity (mL/g) in the range of from 50 to 100, (B) an organic peroxide, (C) a co-crosslinking agent, and (D) specified carbon black.

In addition, Patent Document 3 discloses a fluorine-containing elastomer vulcanizable composition including (a) a vulcanizable fluorine-containing elastomer, (b) a polyol vulcanizing agent containing a polyol compound as a crosslinking agent, and (c) a specified aliphatic amine compound; Patent Document 4 discloses a heat-resistant fluorine rubber composition composed of (a) 100 parts by weight of a fluorine rubber, (b) from 1 to 30 parts by weight of a divalent metal compound (provided that zinc oxide is excluded), (c) from 0.05 to 100 parts by weight of zinc oxide, (d) from 0.05 to 10 parts by weight of a polyhydroxy compound, and (e) from 0.05 to 10 parts by weight of a crosslinking auxiliary agent; and Patent Document 5 discloses a vulcanizable fluorine rubber composition containing (a) a tetrafluoroethylene/perfluoroalkyl vinyl ether copolymer containing an iodine atom and/or a bromine atom, (b) an organic peroxide having a purity of 95% or more, and (c) a co-crosslinking agent having a purity of 95% or more.

However, all of these proposals are concerned with improvements in composition materials, such as an improvement of fluorine rubber species, an improvement in a combination with other rubber or a compounding agent, and the like, and it was difficult to make both a high tensile strength and a high elongation at break compatible with each other.

Then, a more enhancement of mechanical characteristics by a new technique is demanded.

PRIOR ART DOCUMENTS Patent Documents

[Patent Document 1] JP-A-62-841536

[Patent Document 2] JP-A-3-122153

[Patent Document 3] JP-A-6-41378

[Patent Document 4] JP-A-9-188793

[Patent Document 5] JP-A-2002-265733

SUMMARY OF THE INVENTION Problem To Be Solved by the Invention

Under the foregoing circumstances, a problem of the present invention is to provide a fluorine rubber composition which is able to make both a high tensile strength and a high elongation at break after vulcanization compatible with each other and from which favorable mechanical characteristics are obtained even in a high-temperature environment.

Means for Solving Problem

In order to achieve the foregoing object, the present inventors made extensive and intensive investigations. As a result, it has been found that a microstructure in a fluorine rubber composition is controlled by optimizing compounding materials in the composition or improving a kneading method or the like, whereby mechanical characteristics of the fluorine rubber composition after vulcanization may be greatly enhanced.

Specifically, the present invention provides:

-   -   (1) A fluorine rubber composition comprising a rubber component         containing a fluorine rubber, carbon black, and a vulcanization         system compounding agent, wherein     -   the carbon black has a specific surface area by nitrogen         adsorption (N₂SA) of 25 m²/g or more and not more than 180 m²/g         and a dibutyl phthalate (DBP) absorption amount of 60 mL/100 g         or more and not more than 180 mL/100 g; and     -   the vulcanization system compounding agent contains an organic         peroxide and a co-crosslinking agent, and compounding amount of         each component is 0.1 parts by mass or more and not more than         3.0 parts by mass for the organic peroxide component and 0.1         parts by mass or more and not more than 3.0 parts by mass for         the co-crosslinking agent component, respectively based on 100         parts by mass of the rubber component;     -   (2) The fluorine rubber composition as set forth in (1), wherein         a compounding mass ratio of the co-crosslinking agent and the         organic peroxide [ (co-crosslinking agent)/(organic peroxide)]         is 0.3 or more and not more than 0.7;     -   (3) The fluorine rubber composition as set forth in (1) or (2),         wherein a compounding amount of the carbon black is 10 parts by         mass or more and not more than 50 parts by mass based on 100         parts by mass of the rubber component;     -   (4) The fluorine rubber composition as set forth in any one         of (1) to (3), wherein the organic peroxide is a dialkyl         peroxide;     -   (5) The fluorine rubber composition as set forth in any one         of (1) to (4), wherein the co-crosslinking agent is triallyl         isocyanurate;     -   (6) The fluorine rubber composition as set forth in any one         of (1) to (5), further comprising an alkylamine in an amount of         0.1 parts by mass or more and not more than 5.0 parts by mass         based on 100 parts by mass of the rubber component; and     -   (7) A bladder for tire production, which is manufactured using         the fluorine rubber composition as set forth in (1) to (6).

Effect of the Invention

According to the present invention, it is possible to provide a fluorine rubber composition which is able to make both a high tensile strength and a high elongation at break after vulcanization compatible with each other and from which favorable mechanical characteristics are obtained even in a high-temperature environment.

BRIEF DESCRIPTION OF DRAWING

FIG. 1 is a diagrammatic view showing a hermetically closed kneading apparatus which is used in the manufacture of a fluorine rubber composition according to the present invention and an example of the kneading state within the apparatus.

MODES FOR CARRYING OUT THE INVENTION

The present invention is hereunder described with reference to embodiments.

Fluorine Rubber Composition

The fluorine rubber composition of the present embodiment comprises a fluorine rubber and carbon black, wherein the foregoing carbon black has a specific surface area by nitrogen adsorption (N₂SA) of 25 m²/g or more and not more than 180 m²/g and a dibutyl phthalate (DBP) absorption amount of 60 mL/100 g or more and not more than 180 mL/100 g; the foregoing fluorine rubber is at least one member selected among specified kinds of copolymers; and in a kneading step (A) of compounding the foregoing carbon black in the foregoing rubber component, an average shear rate of a rotor surface of a kneading machine is 100 (1/sec) or more, and a kneading maximum temperature T_(m) is 120° C. or higher and not higher than 200° C.

As described above, a fluorine rubber itself is not sufficient in terms of mechanical characteristics, and in order to use the fluorine rubber as a molding material, more durability is required. On the other hand, it is known that carbon black is excellent as a reinforcing agent of rubber, and in particular, the carbon black is a filler indispensable for rubber products which are required to have abrasion resistance or strength.

It is known that when the carbon black is mixed with a general rubber, a gel is formed. Then, it may be considered that mechanical characteristics of the rubber are greatly influenced depending upon what kind of microstructure is formed by this gel within the rubber.

In the present embodiment, it has been found that in view of the fact that even in the case where carbon black is mixed with a fluorine rubber, a gel (so-called “carbon gel”) is formed within the rubber, when a microstructure of the foregoing carbon gel is controlled by optimizing compounding materials by selecting a carbon black species or the like, or devising a kneading method of rubber as described later, or other means, mechanical characteristics of the obtained fluorine rubber composition inclusive of a tensile strength and an elongation at break after vulcanization are greatly improved.

The fluorine rubber composition of the present embodiment contains a rubber component composed of a fluorine rubber and carbon black.

(Fluorine rubber)

The foregoing fluorine rubber is a perfluoro fluorine rubber or a non-perfluoro fluorine rubber, and more specifically, it is at least one member selected among a copolymer of (i) at least one member selected among tetrafluoroethylene, hexafluoropropylene, pentafluoropropylene, trifluoroethylene, chlorotrifluoroethylene, vinyl fluoride, perfluoroalkyl vinyl ether and propylene, and (ii) vinylidene fluoride; a tetrafluoroethylene/perfluoroalkyl vinyl ether copolymer; and a tetrafluoroethylene/propylene copolymer; with a copolymer (especially a binary copolymer or a ternary copolymer) of (i) at least one member selected among tetrafluoroethylene, hexafluoropropylene, pentafluoropropylene, trifluoroethylene, chlorotrifluoroethylene, vinyl fluoride, a perfluoroalkyl vinyl ether and propylene, and (ii) vinylidene fluoride being preferable.

It is preferable that the rubber component in the present embodiment is composed of only a fluorine rubber. However, a small amount of other rubber such as an epichlorohydrin rubber, a silicone rubber, a butyl rubber, a halogenated butyl rubber, etc. may also be compounded within the range where such compounding does not violate the resolution of the problem of the present invention.

(Carbon black)

The carbon black which is compounded in the fluorine rubber composition of the present embodiment is preferably furnace black which is manufactured by the furnace process, and hard black is especially preferable. The hard black as referred to herein indicates SAF, ISAF, HAF, or the like. Then, in the present embodiment, it is necessary that the carbon black to be compounded has a specific surface area by nitrogen adsorption (hereinafter referred to as “N₂SA”) of 25 m²/g or more and not more than 180 m²/g and a dibutyl phthalate absorption amount (hereinafter referred to as “DBP absorption amount”) of 60 mL/100 g or more and not more than 180 mL/100 g.

When the N₂SA is less than 25 m²/g, a reinforcing effect of carbon black is not obtained, whereas when the N₂SA exceeds 180 m²/g, the formation of a carbon black gel becomes excessive, so that each of the prescribed rubber strength and elongation is not obtained. The N₂SA of the carbon black to be used is preferably 30 m²/g or more and not more than 160 m²/g, and more preferably 40 m²/g or more and not more than 150 m²/g.

In addition, when the DBP absorption amount of the carbon black is less than 60 mL/100 g, similar to the case of N₂SA, a reinforcing effect of carbon black is not obtained, when the DBP absorption amount exceeds 180 mL/100 g, also similar to the case of N₂SA, the formation of a carbon black gel becomes excessive, so that each of the prescribed rubber strength and elongation is not obtained. The DBP absorption amount of the carbon black to be used is preferably 70 mL/100 g or more and not more than 160 mL/100 g, and more preferably 80 mL/100 g or more and not more than 150 mL/100 g.

Examples of the carbon black which satisfies the foregoing N₂SA and DBP absorption amount include GPF (N₂SA: 27 m²/g, DBP absorption amount: 87 mL/100 g), FEF (N₂SA: 42 m²/g, DBP absorption amount: 115 mL/100 g), LI-HAF (N₂SA: 74 m²/g, DBP absorption amount: 103 mL/100 g), HAF (N330, N₂SA: 77 m²/g, DBP absorption amount: 101 mL/100 g), N-339 (N₂SA: 83 m²/g, DBP absorption amount: 128 mL/100 g), N-351 (N₂SA: 74 m²/g, DBP absorption amount: 124 mL/100 g), IISAF (N285, N ₂SA: 98 m²/g, DBP absorption amount: 124 mL/100 g), ISAF (N220, N₂SA: 115 m²/g, DBP absorption amount: 113 mL/100 g), N-234 (N₂SA: 124 m²/g, DBP absorption amount: 125 mL/100 g) SAF (N110, N₂SA: 139 m²/g, DBP absorption amount: 113 mL/100 g), SAF-HS (N₂SA: 142 m²/g, DBP absorption amount: 130 mL/100 g), and the like.

Of these, LI-HAF, HAF, and ISAF are especially preferable.

The foregoing carbon black can be, for example, used in an amount of preferably 10 parts by mass or more and not more than 50 parts by mass, more preferably 10 parts by mass or more and not more than 40 parts by mass, and especially preferably 15 parts by mass or more and not more than 35 parts by mass based on 100 parts by mass of the rubber component.

Incidentally, the foregoing carbon black may be used alone or in combination of plural kinds thereof.

(Vulcanization system compounding agent)

Examples of the vulcanization system compounding agent which is further compounded in the fluorine rubber composition of the present embodiment include an organic peroxide, a co-crosslinking agent, and a metal compound as a crosslinking auxiliary agent which is compounded, if desired.

The organic peroxide is not particularly limited so far as it has a function as a crosslinking agent, and examples thereof include benzoyl peroxide, tert-butyl hydroperoxide, 2,4-bichlorobenzoyl peroxide, di-tert-butyl peroxide, dicumyl peroxide, Cert-butylcumyl peroxide, 1,1-di (tert-butylperoxy)-3,3,5-trimethylcyclohexane, 2,5-dimethyl-2,5-di (tert-butylperoxy) hexane, 2,5-dimethyl-2,5-di (tert-butylperoxy) hexine-3, 1,3-di (2-tert-butylperoxyisopropyl)benzene, 2,5 -dimethyl-2,5-di (benzoylperoxy) hexane, tert-butyl peroxybenzoate, tert-butyl peroxyisopropyl carbonate, n-butyl-4,4-di(tert-butylperoxy)valerate, 2,5-dimethylhexane-2,5-di(peroxylbenzoate), and the like.

Of these, dialkyl peroxides such as 2,5-dimethyl-2,5-di (tert-butylperoxy) hexane, etc. are especially preferable.

The foregoing organic peroxide can be used in an amount of preferably 0.1 parts by mass or more and not more than 3.0 parts by mass, more preferably 0.2 parts by mass or more and not more than 2.5 parts by mass, and especially preferably 0.3 parts by mass or more and not more than 2.0 parts by mass based on 100 parts by mass of the rubber component. When the compounding amount of the organic peroxide is 0.1 parts by mass or more and not more than 3.0 parts by mass, it is possible to control a design of balance between high-temperature elongation and strength.

The foregoing organic peroxide may be used alone or in combination of plural kinds thereof.

In addition, as the co-crosslinking agent which is further compounded in the fluorine rubber composition of the present embodiment, for example, triallyl isocyanurate (TAIC), triallyl cyanurate, diallyl phthalate, trivinyl isocyanurate, tri (5-norbornene-2-methylene) cyanurate, 1,3-butylene glycol dimethacrylate, 1,4-butylene glycol dimethacrylate, ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, triethylene glycol dimethacrylate, tetraethylene glycol dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, triallyl formal, triallyl trimellitate, dipropargyl terephthalate, tetraallyl terephthalate amide, triallyl phosphate, fluorinated triallyl isocyanurate (1,3,5-tris(2,3,3-trifluoro-2-propenyl)-1,3,5-triazine-2,4,6-trione), triallyl phosphite, N,N-diallyl acrylamide, hexaallyl phosphoramide, N,N,N′,N′-tetraallyl tetraphthalamide, N,N,N′,N′-tetraallyl malonamide, 2,4,6-trivinyl methyltrisloxane, triallyl phosphite, and the like can be used. However, it should not be construed that the present invention is limited thereto.

Among the foregoing co-crosslinking agents, in view of vulcanization properties and physical properties of vulcanizates, triallyl isocyanurate (TAIC) is preferable.

The foregoing co-crosslinking agent is preferably used in an amount of 0.1 parts by mass or more and not 3.0 parts by mass based on 100 parts by mass of the rubber component. So far as the compounding amount falls within the foregoing range, it is possible to control a design of balance between high-temperature elongation and strength. The co-crosslinking agent can be used in an amount of more preferably 0.3 parts by mass or more and not more than 2.5 parts by mass, and especially preferably 0.5 parts by mass or more and not more than 2.0 parts by mass based on 100 parts by mass of the rubber component.

Incidentally, the foregoing co-crosslinking agent may be used alone or in combination of plural kinds thereof.

In addition, examples of the metal compound as the crosslinking auxiliary agent which is compounded in the fluorine rubber composition of the present embodiment, if desired include a metal oxide and a metal hydroxide each functioning as an acid acceptor (a material having chiefly an action to absorb an acidic substance produced by vulcanization).

Examples of the metal oxide include zinc white (ZnO), magnesium oxide, lead oxide, calcium oxide, zinc oxide, iron oxide, titanium oxide, silicon oxide, aluminum oxide, and the like. Of these, divalent metal oxides such as zinc white (ZnO) magnesium oxide, calcium oxide, etc. are preferable.

The foregoing metal compound can be, for example, used in an amount of preferably 0 part by mass or more and not more than 20 parts by mass, more preferably 0 part by mass or more and not more than 15 parts by mass, and especially preferably 1 part by mass or more and not more than 10 parts by mass based on 100 parts by mass of the fluorine rubber that is the rubber component.

The foregoing metal compound may be used alone or in combination of plural kinds thereof.

In the fluorine rubber composition of the present embodiment, in addition to the foregoing components, for example, a compounding agent which is generally used in the rubber industries, inclusive of a reinforcing agent such as a carbon fiber, etc.; a filler such as calcium carbonate, magnesium carbonate, aluminum hydroxide, magnesium hydroxide, aluminum silicate, magnesium silicate, calcium silicate, potassium titanate, titanium oxide, barium sulfate, aluminum borate, a glass fiber, an aramid fiber, diatomaceous earth, wollastonite, etc.; a processing aid such as a wax, a metallic soap, a carnauba wax, an alkylamine, etc.; an anti-aging agent; a thermoplastic resin; a clay; other fibrous filler; and the like, can be compounded as the need arises within the range where the effects of the organic peroxide and the co-crosslinking agent which are used in the present embodiment are not impaired.

Incidentally, as for the foregoing materials, it is preferable that the processing aid is contained in an amount of 0.1 parts by mass or more and not more than 10 parts by mass based on 100 parts by mass of the rubber component, and in particular, the alkylamine is contained in an amount of preferably 0.1 parts by mass or more and not more than 5.0 parts by mass, and more preferably 0.5 parts by mass or more and not more than 3.0 parts by mass. In addition, examples of the foregoing alkylamine include Farmine 86T (manufactured by Kao Corporation) and Armeen 18D (manufactured by Akzo Nobel).

In order to allow the fluorine rubber composition of the present embodiment to contain a rubber component containing a fluorine rubber and carbon black as described above and to form a suitable microstructure on the basis of the foregoing carbon gel, it is necessary to perform the kneading step (A) of compounding the carbon black in the rubber component in the following manner.

That is, first of all, an average shear rate of a rotor tip point of a kneading machine (the roll surface in the case where the kneading machine is a roll) in the kneading step (A) is set up to 100 (1/sec) or more. When the average shear rate is less than 100 (1/sec), it may be impossible to disperse the carbon black to an extent of an aggregate unit to form a favorable carbon gel network reinforcing structure.

The foregoing average shear rate is preferably 300 (1/sec) or more, and more preferably 1,000 (1/sec) or more.

Here, when a rotor diameter is defined as R, a rotor chip point clearance is defined as C, and a rotor rotation rate is defined as N (rpm), the foregoing average shear rate (γ, 1/sec) can be determined by γ=π·R·N/15 C (π: ratio of the circumference of a circle to its diameter).

In addition, a kneading maximum temperature T_(m) of the kneading step (A) of compounding carbon black in the foregoing rubber component is allowed to be 120° C. or higher and not higher than 200° C. When the kneading maximum temperature T_(m) is 120° C. or higher and not higher than 200° C., the so-called “carbon gel” which is a gel obtained through binding of the fluorine rubber and the carbon black without causing decomposition of the rubber component or the like is suitably produced, and therefore, it is possible to make both a high tensile strength and a high elongation at break compatible with each other. From such a viewpoint, the T_(m) is more preferably 140° C. or higher and not higher than 170° C., and still more preferably 155° C. or higher and not higher than 165° C.

Incidentally, the kneading maximum temperature T_(m) is detected by installing a temperature sensor in plural places within the kneading machine.

A typical hermetically closed kneading apparatus which is used in the present embodiment is hereunder described. FIG. 1 is a diagrammatic view showing a hermetically closed kneading apparatus which is used in the manufacture of the fluorine rubber composition of the present embodiment and an example of the kneading state within the apparatus.

The hermetically closed kneading apparatus shown in FIG. 1 is a batch hermetically closed kneading apparatus of a tangent type single-blade system and is called an “internal mixer”. This hermetically closed kneading apparatus 10 is constructed of a kneading machine 11 and a power unit 21, and a hydraulic cylinder 19 and guide rods 20. This kneading machine 11 is constructed of a combination of a kneading machine main body 12 and a floating weight 18. The kneading machine main body 12 forms a kneading chamber 13 having a shape in which two cylindrical faces shaped in a semicircular cross section are united. An opening 14 formed on the cylindrical faces is provided above the kneading chamber 13.

Incidentally, as for the foregoing internal mixer, a Banbury type or pressure kneader is generally used.

In a central axis of the semicircular cylindrical faces of the foregoing kneading chamber 13, a pair of rotors 15 a and 15 b is provided, and the first rotor 15 a has a rotation axis 16 a, whereas the second rotor 15 b has a rotation axis 16 b. The first rotor 15 a and the second rotor 15 b are provided with a first blade 17 a and a second blade 17 b, respectively. The pair of the rotors 15 a and 15 b are constructed in such a manner that they are mutually rotated by the power unit 21 toward a space between the both on the first and second rotation axes 16 a and 16 b and that the rubber component and the rubber compounding materials such as carbon black, etc. are kneaded by the mutual first blade 17 a and second blade 17 b while applying a shear, thereby manufacturing a mixture 1.

The floating weight 18 is provided with a peripheral surface 18 a engaged with the inside of the opening 14 of the kneading machine main body 12 and achieves immobilization and pressure contact such that the rubber component and the rubber compounding materials such as carbon black, etc. are easily mixed with each other by the pressure from the hydraulic cylinder 19 and the guide rods 20. As for the shape of the floating weight, though a seagull type is better than a semicircular type, a Banbury type may also be adopted.

In FIG. 1, while the hermetically closed kneading apparatus having a batch hermetically closed kneading apparatus of a tangent type single-blade system has been shown, an engagement type single-blade system, a tangent type double-blade system or an engagement type double-blade system (provided with two rotors having two blades), or a tangent type triple-blade system or an engagement type triple-blade system (provided with two rotors having three blades) is similarly used.

In an open roll which is of an open system, it is usually difficult to increase the kneading maximum temperature T_(m), and therefore, in that case, it is not preferable to use the open roll in the kneading step according to the present embodiment.

In the kneading step (A) (sometimes referred to as “masterbatch step”), in general, the rubber component is first thrown into the kneading machine, and after kneading for from 10 seconds to several minutes, the carbon black is thrown. The whole amount of the carbon black may be thrown at once, or the carbon black may be dividedly thrown several times.

Since the time when throwing of the carbon black into the kneading machine is completed, a power applied to the rotors of the kneading machine increases, and thereafter, the power decreases step by step, whereby the kneading step is terminated. The mixture of the rubber component and the carbon black, etc. is discharged from the kneading machine, whereby the kneading step (A) is terminated. The mixture after termination of the kneading step (A) is formed into a sheet by rolls (underrolls in the Banbury type kneading machine) and transferred into a next step.

After termination of the foregoing kneading step (A), the obtained mixture is cooled, and if desired, after going through an aging step (allowing to stand at room temperature (about 23° C.)), in general, the obtained mixture is formed into a vulcanizable fluorine rubber composition by a kneading step (B) of compounding the foregoing vulcanization system compounding agent.

Incidentally, if desired, a step of again kneading the mixture obtained in the kneading step (A) (also referred to as “masterbatch remill step” or “X-mill step”) may be performed between the kneading step (A) and the kneading step (B).

In addition, as for a specific kneading apparatus for performing the kneading step (A) and the kneading step (B), for example, a Banbury mixer, a kneader, a uniaxial kneading machine, a biaxial kneading machine, and the like can be used in the kneading step (A); and the kneading machines which are used in the foregoing kneading step (A), a roll, a mill blender, and the like can be used in the kneading step (B).

The vulcanizable fluorine rubber composition obtained by the above-described method is molded into a vulcanized article by means of pressurization, heating, and vulcanization.

Specifically, the foregoing vulcanizable fluorine rubber composition is usually heated at a temperature of from 140° C. to 230° C. under pressure for from about 1 to 120 minutes using an injection molding machine, a compression molding machine, a vulcanization press machine, an oven, or the like, to achieve crosslinking (vulcanization), whereby a vulcanized article can be molded. The foregoing vulcanization is a step of achieving crosslinking for forming a fixed shape. For a complicated shape, though the vulcanized article is preferably molded using a die, it may be possible to achieve the vulcanization even using an oven by means of air heating or the like.

In the present embodiment, secondary vulcanization can also be performed as the need arises. In the case of performing the secondary vulcanization, though the same method as described above may be performed, for example, a heat treatment may be performed at a temperature in the range of from 140° C. to 230° C. for from 1 to 20 hours depending upon an application.

It is desirable that the thus-obtained fluorine rubber composition of the present embodiment has the following mechanical characteristics after vulcanization.

Specifically, first of all, it is desirable that after vulcanization, a tensile strength at 25° C. is 10 MPa or more and not more than 50 MPa, and an elongation at break at 25° C. is 400% or more and not more than 800%; and a tensile strength at 160° C. is 1 MPa or more and not more than 20 MPa, and an elongation at break at 160° C. is 150% or more and not more than 500%.

In view of the fact that the tensile strength at 25° C. and the elongation at break at 25° C. fall within the foregoing ranges, it becomes possible to newly apply the fluorine rubber composition to the industrial fields where it has hitherto been considered to be impossible to use fluorine rubber compositions due to a deficiency in mechanical strength or the like. In addition to the above, in view of the fact that the tensile strength at 160° C. and the elongation at break at 160° C. fall within the foregoing ranges, it becomes possible to apply the fluorine rubber composition even to the fields where it is required to make both heat resistance and mechanical characteristics compatible with each other, so that the application as a fluorine rubber composition is expanded to an extent that the application has not been realized up to date.

Incidentally, the foregoing elongation at break and tensile strength are measured in conformity with JIS K 6251:2004. In addition, the foregoing tear strength is measured in conformity with JIS K 6252:2001.

Bladder for Tire Production

The bladder for tire production of the present embodiment is manufactured using the fluorine rubber composition of the foregoing present embodiment. Specifically, the foregoing bladder can be obtained by molding and vulcanizing the fluorine rubber composition of the present embodiment.

In general, in a tire production step, there are used roughly classified two kinds of bladders inclusive of a bladder for tire molding to be used at the time of assembling respective constituent members of a tire to mold a green tire (unvulcanized tire) and a bladder for tire vulcanization to be used for giving an ultimate product tire shape at the time of vulcanization. The fluorine rubber composition of the present embodiment can be used for the manufacture of all of the foregoing bladders.

In particular, in view of the fact that the bladder for tire molding of the present embodiment uses the fluorine rubber composition of the foregoing present embodiment, it does not require conventional silicone coating, has a high strength as compared with the conventional techniques, and is able to greatly enhance a use life. Also, the bladder for tire molding of the present embodiment has a high tear strength as compared with the conventional techniques. In addition, in view of the fact that the bladder for tire vulcanization of the present embodiment uses the fluorine rubber composition of the foregoing present embodiment, its coefficient of friction is small, and its release properties are greatly enhanced. Therefore, it is possible to prevent the adhesion between the bladder and the green tire from occurring without coating with a release agent. Thus, not only the conventional coating step with a release agent can be omitted, and adverse influences against the tire quality can be prevented, but it is possible to greatly enhance the use life.

EXAMPLES

The present invention is hereunder described in more detail with reference to the following Examples, but it should be construed that the present invention is not limited thereto at all.

The characteristics were measured according to the following methods.

-   -   (1) Elongation at break (%) and tensile strength (MPa):

The measurement was performed at 25° C. and 160° C. in conformity with JIS K 6251:2004. As for samples, a dumbbell No. 3 shape was used with respect to the results shown in Table 1, and a dumbbell No. 6 shape was used with respect to the results shown in Table 2 (thickness of a parallel portion of each of the dumbbells: 2 mm).

-   -   (2) Tear strength (N/mm):

The measurement was performed at 23° C. and 160° C. in conformity with JIS K 6252:2001. As for samples, an unnotched angle shape (thickness: 2 mm) was used.

-   -   (3) Fatigue resistance:

A De Mattia flex-cracking test was performed at 25° C. in conformity with JIS K 6260:1999, and a number of double bends reaching the breakage was determined.

Examples A1 to A2 and Comparative Examples A1 to A6

(Manufacture of fluorine rubber composition)

According to each of compoundings shown in Table 1, the kneading step (A) of kneading components exclusive of a co-crosslinking agent and an organic peroxide with a fluorine rubber and carbon black was carried out under a condition shown in the table, and when a. kneading temperature reached a maximum temperature T_(m), the kneaded material was released to obtain a masterbatch (mixture). Incidentally, a hermetically closed mixer having a kneading capacity of one liter (DS1-5MHB-E Model kneader, manufactured by Moriyama Company Ltd.) was used as a kneading machine, and a 10-inch roll (manufactured by Sakurai Roll K. K.) was used as a roll type.

After going through an aging step of allowing the masterbatch obtained in the kneading step (A) to stand at room temperature (23° C.) for 12 hours, a co-crosslinking agent and an organic peroxide shown in Table 1 were added to the foregoing masterbatch, and the contents were kneaded at 100° C. using an 8-inch open roll (kneading step (B)), thereby obtaining a vulcanizable fluorine rubber composition. Incidentally, zinc white and an alkylamine may be added in the kneading step (A), may be added in the kneading step (B), or may be dividedly added in the kneading steps (A) and (B).

(Evaluation)

The obtained vulcanizable fluorine rubber composition (unvulcanized) was processed into a sheet form and then subjected to press vulcanization in a die under a condition at a pressure of 2.0 MPa and a temperature of 160° C. for 30 minutes, thereby obtaining a sheet having a thickness of 2 mm. The obtained sheet of the vulcanized fluorine rubber composition was used and measured for the shear modulus by the dynamic viscoelasticity test, the elongation at break, the tensile strength, the tear strength, and the fatigue resistance by the foregoing methods. On the other hand, a sheet of the foregoing unvulcanized fluorine rubber composition was separately measured for the shear modulus by the dynamic viscoelasticity test.

The results are shown in Table 1.

TABLE 1 Com- Compar- Exam- Exam- parative ative ple ple Comparative Comparative Comparative Comparative Exam- Exam- A1 A2 Example A1 Example A2 Example A3 Example A4 ple A5 ple A6 Compounding Fluorine rubber*¹ 100 100 100 100 100 100 100 100 formulation Carbon black-A*² — — 30 — — — — — (parts by mass) Carbon black-B*³ — 30 — — — — — — Carbon black-C*⁴ 30 — — 30 30 60 30 30 Zinc white 3.0 3.0 3.0 3.0 3.0 3.0 3.0 3.0 Co-crosslinking agent*⁵ 0.5 0.5 0.5 0.5 0.5 0.5 0.5 3.0 Organic peroxide*⁶ 2.5 2.5 2.5 2.5 2.5 2.5 2.5 8.0 Alkylamine*⁷ 1.0 1.0 1.0 1.0 1.0 1.0 — 1.0 Kneading Kneading machine Mixer Mixer Mixer Roll Mixer Mixer Mixer Mixer condition Shear rate (1/sec) 300 300 300 10 300 300 300 300 Maximum temperature (° C.) 165 165 165 110 210 165 165 165 Physical Elongation at break (% at 25° C.) 500 400 400 300 250 200 500 150 characteristics Tensile strength (MPa at 25° C.) 25 20 12 15 30 25 25 26 Tear strength (N/mm at 25° C.) 50 30 15 10 30 40 50 50 Elongation at break (% at 160° C.) 340 200 100 120 80 60 140 70 Tensile strength (MPa at 160° C.) 8 4 2 1.5 10 8 3 9 Tear strength (N/mm at 160° C.) 12 5 2 0.7 0.5 0.5 2.8 0.7 Fatigue resistance 20000 10000 100 90 60 10 500 1 (number of times at 25° C.) [Note] *¹Fluorine rubber: A copolymer of vinylidene fluoride, hexafluoropropylene, and tetrafluoroethylene, a trade name: GBL600S, manufactured by DuPont Elastomer Co., Ltd. *²Carbon black-A: MT (N₂SA: 12 m²/g, DBP absorption amount: 41 mL/100 g), a trade name: Thermax N-990, manufactured by Cancarb *³Carbon black-B: GPF (N₂SA: 27 m²/g, DBP absorption amount: 87 mL/100 g), a trade name: Asahi #60, manufactured by Asahi Carbon Co., Ltd. *⁴Carbon black-C: ISAF (N₂SA: 119 m²/g, DBP absorption amount: 114 mL/100 g), a trade name: Seast 6, manufactured by Tokai Carbon Co., Ltd. *⁵Co-crosslinking agent: Triallyl isocyanurate, a trade name: Diak-7, manufactured by DuPont Elastomer Co., Ltd. *⁶Organic peroxide: 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane, a trade name: Perhexa 25B40 (active ingredient: 40%), manufactured by NOF Corporation *⁷Alkylamine: A monoalkyl primary amine, a trade name: Armeen 18D, manufactured by Akzo Nobel

Examples B1 to B7 and Comparative Examples B1 to B4

(Manufacture of fluorine rubber composition)

According to each of compoundings shown in Table 2, the kneading step (A) of kneading components exclusive of a co-crosslinking agent and an organic peroxide with a fluorine rubber and carbon black was carried out under a condition shown in the table, and when a kneading temperature reached a maximum temperature T_(m), the kneaded material was released to obtain a masterbatch (mixture). Incidentally, a 0.5-liter hermetically closed mixer (MIX-LABO, manufactured by Moriyama Company Ltd.) and a 35-liter hermetically closed mixer (manufactured by Toshin Co., Ltd.) were used as a mixer type kneading machine, and an 8-inch roll (manufactured by Kansai Roll Co., Ltd.) and a 22-inch roll (manufactured by Kobe Kikai K. K.) were used as a roll type.

After going through an aging step of allowing the masterbatch obtained in the kneading step (A) to stand at room temperature (23° C.) for 12 hours, a co-crosslinking agent and an organic peroxide shown in Table 2 were added to the foregoing masterbatch, and the contents were kneaded at 100° C. using an 8-inch open roll (kneading step (B)), thereby obtaining a vulcanizable fluorine rubber composition. Incidentally, zinc white and an alkylamine may be added in the kneading step (A), may be added in the kneading step (B), or may be dividedly added in the kneading steps (A) and (B).

(Evaluation)

The obtained vulcanizable fluorine rubber composition (unvulcanized) was processed into a sheet form and then subjected to press vulcanization in a die under a condition at a pressure of 2.0 MPa and a temperature of 160° C. for 30 minutes, thereby obtaining a sheet having a thickness of 2 mm. The obtained sheet of the vulcanized fluorine rubber composition was used and measured for the shear modulus by the dynamic viscoelasticity test, the elongation at break, the tensile strength, the tear strength, and the fatigue resistance by the foregoing methods. On the other hand, a sheet of the foregoing unvulcanized fluorine rubber composition was separately measured for the shear modulus by the dynamic viscoelasticity test.

The results are shown in Table 2.

TABLE 2 Example Example Example Example Example Example B1 B2 B3 B4 B5 B6 Compounding Fluorine rubber-A*1 100 — — 100 100 100 formulation Fluorine rubber-B*2 — 100 100 — — — (parts by mass) Carbon black-A*3 — — — — — — Carbon black-B*4 — — 20 — — — Carbon black-C*5 20 20 — — — 30 Carbon black-D*6 — — — 30 45 — Zinc white 1.0 1.0 1.0 1.0 1.0 1.0 Co-crosslinking agent*7 0.83 0.83 0.83 0.83 1.67 2.5 Organic peroxide*8 1.88 1.88 1.88 2.5 2.5 2.5 Alkylamine*9 1.0 1.0 1.0 1.0 1.0 1.0 Kneading Kneading machine Mixer Mixer Mixer Mixer Mixer Mixer condition Shear rate (1/sec) 829 829 829 829 829 1561 Maximum temperature (° C.) 179 164 158 175 164 2147 Physical Elongation at break (% at 25° C.) 580 410 440 520 420 550 characteristics Tensile strength (MPa at 25° C.) 17.4 21.6 11.1 16.6 18 16.8 Tear strength (N/mm at 25° C.) 42.9 34.4 30.8 43.4 45.7 49.1 Elongation at break (% at 160° C.) 400 190 160 350 210 400 Tensile strength (MPa at 160° C.) 5.7 4.6 2.4 6.1 6.5 5.4 Tear strength (N/mm at 160° C.) 15.7 13.2 9.6 15.3 15 20.4 Fatigue resistance >20000 >20000 >20000 >20000 >20000 >20000 (number of times at 25° C.) Example Comparative Comparative Comparative Comparative B7 Example B1 Example B2 Example B3 Example B4 Compounding Fluorine rubber-A*1 100 — — 100 — formulation Fluorine rubber-B*2 — 100 100 — 100 (parts by mass) Carbon black-A*3 — 20 — — — Carbon black-B*4 — — 20 — 20 Carbon black-C*5 30 — — 30 — Carbon black-D*6 — — — — — Zinc white — 1.0 1.0 — 1.0 Co-crosslinking agent*7 2.5 0.83 0.83 2.5 6.7 Organic peroxide*8 2.5 1.88 1.88 2.5 1.88 Alkylamine*9 1.0 1.0 1.0 1.0 1.0 Kneading Kneading machine Mixer Mixer Roll Mixer Mixer condition Shear rate (1/sec) 1493 829 84 1800 829 Maximum temperature (° C.) 1702 152 70 219 157 Physical Elongation at break (% at 25° C.) 490 540 360 270 240 characteristics Tensile strength (MPa at 25° C.) 18.7 10.5 9.4 7.4 17 Tear strength (N/mm at 25° C.) 45.2 20.6 24.9 51.2 38.3 Elongation at break (% at 160° C.) 300 60 120 80 100 Tensile strength (MPa at 160° C.) 5.4 1.3 2.3 2 4.9 Tear strength (N/mm at 160° C.) 18.2 5.4 7.2 7.8 10.8 Fatigue resistance >20000 >20000 300 18 3000 (number of times at 25° C.) [Note] *¹Fluorine rubber-A: A binary copolymer of vinylidene fluoride and hexafluoropropylene, a trade name: G801, manufactured by Daikin Industries, Ltd. *²Fluorine rubber-B: A ternary copolymer of vinylidene fluoride, tetrafluoroethylene, and hexafluoropropylene, a trade name: G9074, manufactured by Daikin Industries, Ltd. *³Carbon black-A: MT (N₂SA: 12 m²/g, DBP absorption amount: 41 mL/100 g), a trade name: N990, manufactured by Cancarb Thermix *⁴Carbon black-B: GPF (N₂SA: 27 m²/g, DBP absorption amount: 26 mL/100 g), a trade name: Seast V, manufactured by Tokai Carbon Co., Ltd. *⁵Carbon black-C: ISAF (N₂SA: 119 m²/g, DBP absorption amount: 114 mL/100 g), a trade name: Seast 6, manufactured by Tokai Carbon Co., Ltd. *⁶Carbon black-D: HAF (N₂SA: 79 m²/g, DBP absorption amount: 101 mL/100 g), a trade name: Seast 3, manufactured by Tokai Carbon Co., Ltd. *⁷Co-crosslinking agent: Triallyl isocyanurate (TAIC), a trade name: TAIC (registered trademark), manufactured by Nippon Kasei Chemical Co., Ltd. *⁸Organic peroxide: 2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane, a trade name: Perhexa 25B40, manufactured by NOF Corporation *⁹Alkylamine: Stearylamine, a trade name: Farmine 86T, manufactured by Kao Corporation

Performance of Bladder for Tire Production

A bladder for tire vulcanization and a bladder for tire molding were fabricated, respectively by using each of a conventionally used butyl compounded rubber composition and the fluorine rubber compositions of Examples A1 and B1.

Using the obtained bladder for tire vulcanization, vulcanization of a tire having a tire size of PSR215/60R15.5 was carried out for a vulcanization time of 15 minutes without coating a release agent on the bladder surface and the inner surface of the green tire until the bladder was punctured, thereby evaluating its use life (number of times of vulcanization). In addition, as for the bladder for tire molding, the number of tires which can be molded was evaluated in the same manner using a general tire for passenger car. However, as for the bladder for tire vulcanization using the conventionally used butyl compounded rubber composition, a release agent was coated on the bladder surface and the inner surface of the green tire.

As a result, the use life of the bladder for tire vulcanization was 300 times for the bladder using the conventional rubber composition, whereas it was 2,000 times for the bladder using each of the fluorine rubber compositions of Examples A1 and B1.

In addition, the number of tires which can be molded on the bladder for tire molding was 3,000 for the bladder using the conventional rubber composition, whereas it was 10,000 for the bladder using each of the fluorine rubber compositions of Examples A1 and B1. 

1. A fluorine rubber composition comprising a rubber component containing a fluorine rubber and carbon black, wherein the carbon black has a specific surface area by nitrogen adsorption (N₂SA) of 25 m²/g or more and not more than 180 m²/g and a dibutyl phthalate (DBP) absorption amount of 60 mL/100 g or more and not more than 180 mL/100 g; the fluorine rubber is at least one member selected among a copolymer of (i) at least one monomer selected among tetrafluoroethylene, hexafluoropropene, pentafluoropropene, trifluoroethylene, chlorotrifluoroethylene, vinyl fluoride, perfiuoroalkyl vinyl ether and propylene, and (ii) vinylidene fluoride; a tetrafluoroethylene/perfluoroalkyl vinyl ether copolymer; and a tetrafluoroethylene/propylene copolymer; and in a kneading step (A) of compounding the carbon black in the rubber component, an average shear rate of a rotor tip point of a kneading machine is 100 (1/sec) or more, and a kneading maximum temperature T_(m) is 120° C. or higher and not higher than 200° C.
 2. The fluorine rubber composition according to claim 1, wherein a compounding amount of the carbon black is 10 parts by mass or more and not more than 50 parts by mass based on 100 parts by mass of the rubber component.
 3. The fluorine rubber composition according to claim 1, further comprising a vulcanization system compounding agent, wherein the vulcanization system compounding agent contains an organic peroxide and a co-crosslinking agent; and a compounding amount of the organic peroxide component is 0.1 parts by mass or more and not more than 3.0 parts by mass, and a compounding amount of the co-crosslinking agent component is 0.1 parts by mass or more and not more than 3.0 parts by mass based on 100 parts by mass of the rubber component.
 4. The fluorine rubber composition according to claim 1, wherein the organic peroxide is a dialkyl peroxide.
 5. The fluorine rubber composition according to claim 1, wherein the co-crosslinking agent is triallyl isocyanurate.
 6. The fluorine rubber composition according to claim 1, further comprising an alkylamine in an amount of 0.1 parts by mass or more and not more than 5.0 parts by mass based on 100 parts by mass of the rubber component.
 7. A bladder for tire production, which is manufactured using the fluorine rubber composition according to claim